Waarmtebestindich stiel castings en10295
Us bedriuw produseart hjittefresinte stiel yn oerienstimming mei Jeropeeske noarmen, leverje it ferwurkjen fan oanpassing, wolkom om te keap
Meganyske eigenskippen bykeamertemperatuer
|
Oantsjutting |
Hjitte behanneling |
Trekkraft toets |
Hurdens Hb Maks. |
||||||
|
Symboal |
Temperatuer graad |
FPO, 2 Mpa a min. |
RM Mpa a min. |
A % min. |
|||||
|
Namme |
Nûmer |
||||||||
|
Ferritic and Austenitic - Ferritic-graden |
GX30CRSIZ B |
1.4710 |
+ AC |
800 oant 850 |
300 |
||||
|
GX40CRSI13 |
1.4729 |
+ AC |
800 oant 850 |
300 |
|||||
|
GX40CRSI17 |
1.4740 |
+ AC |
800 oant 850 |
300 |
|||||
|
GX40CRS24 |
1.4745 |
Nee hjitte behanneling |
d |
||||||
|
Gx40crsi28 |
1.4776 |
d |
|||||||
|
Gx130crsi29 |
1.4777 |
d |
|||||||
|
GX160CRI18 |
1.4743 |
d |
|||||||
|
GX40CRnisi 27-4 |
1.4823 |
250 |
550 |
3 |
d |
||||
|
Austenitic-graden |
GX25CRNISI 18-9 |
1.4825 |
230 |
450 |
15 |
||||
|
GX40CRnisi 22-10 |
1.4826 |
230 |
450 |
8 |
|||||
|
GX25CRNISI 20-14 |
1.4832 |
230 |
450 |
10 |
|||||
|
GX40CRnisi 25-12 |
1.4837 |
220 |
450 |
6 |
|||||
|
GX40CRnisi 25-20 |
1.4848 |
220 |
450 |
8 |
|||||
|
GX40CRnisinB 24-24 |
1.4855 |
220 |
450 |
4 |
|||||
|
GX35NicRsi 25-21 |
1.4805 |
220 |
430 |
8 |
|||||
|
GX40NicRsi 35-17 |
1.4806 |
220 |
420 |
6 |
|||||
|
GX40Nicrsinb 35-18 |
1.4807 |
220 |
420 |
4 |
|||||
|
GX40NicRsi 38-19 |
1.4865 |
220 |
420 |
6 |
|||||
|
GX40Nicrsinb 38-19 |
1.4849 |
220 |
420 |
4 |
|||||
|
GX10Nicrsinb 32-20 |
1.4859 |
180 |
440 |
20 |
|||||
|
GX40NicRsi 35-26 |
1.4857 |
220 |
440 |
6 |
|||||
|
GX40Nicrsinb 35-26 |
1.4852 |
220 |
440 |
4 |
|||||
|
GX50NicrCO 20-20-20 |
1.4874 |
320 |
420 |
6 |
|||||
|
GX50NicRcow 35-25- 15-5 |
1.4869 |
270 |
480 |
5 |
|||||
|
GX40Nicrnb 45-35 |
1.4889 |
240 |
440 |
3 |
|||||
|
Nikkel en Kobalt |
Base Alloys |
G-NICR28W |
2.4879 |
240 |
440 |
3 |
|||
|
G -cocr28 |
2.4778 |
235 |
490 |
6 |
|||||
|
G-nicr50nb |
2.4680 |
230 |
540 |
8 |
|||||
|
G-Nicr15 |
2.4815 |
200 |
400 |
3 |
|||||
|
A 1MPA =1 n / mm2 b As dizze klasse wurdt brûkt foar wear-resistinte custives, dan kinne se wurde levere sûnder hjittensbehandeling . C + A MEID: annealing D CAILINGS kinne ek levere wurde yn 'e ureare tastân yn hokker gefal in maksimale hurdheidswearde is oerienkommen . |
|||||||||